Naslov (srp)

Karakteristike niklenog katalizatora na perlitu sintetisanog pri različitim molskim odnosima nikla i magnezijuma : doktorska disertacija

Autor

Radonjić, Vojkan D., 1984-

Doprinosi

Nedić Vasiljević, Bojana, 1983-
Lončarević, Davor
Krstić, Jugoslav, 1968-
Stanisavljev, Dragomir, 1960-
Milojević-Rakić, Маја, 1982-

Opis (srp)

U okviru ove doktorske disertacije ispitivana je mogućnost sinteze aktivnog niklenogkatalizatora modifikovanog magnezijumom u reakciji hidrogenizacije suncokretovog ulja,upotrebom perlita kao nosača katalizatora. Da bi se ispitala moguća aktivacija odabranog perlitnognosača (PF-295), on je tretiran u destilovanoj vodi na 90 °C, u 10 % rastvoru Na2CO3 na 90 °C i u 9mol/dm3 HCl-u uz refluks na 100 °C. Karakterizacijom nosača nisu uočene značajne razlike umorfologiji, teksturi i strukturi dobijenih materijala.Za sintezu prekursora na različito tretiranim nosačima korišćen je precipitacionodepozicioni postupak, upotrebom čvrstog Na2CO3 kao taložnog agensa nikl (nNi:nSiO2 = 1) imagnezijum (nMg:nNi = 0,1) vrsta. Rezultati karakterizacija prekursora su pokazali da među njimane postoje značajne razlike, osim u vrednostima disperznosti (određene hemisorpcijom H2). Takođesu uočene manje razlike u aktivnosti sintetisanih katalizatora u katalitičkim testovimahidrogenizacije suncokretovog ulja.Upotrebom različitih molskih odnosa (nNi:nSiO2 i nMg:nNi) dobijene su dve serije prekursorakoje su okarakterisane morfološki, teksturalno i strukturno. Prekursori serije sa različitim sadržajemNi pokazali su razlike u rezultatima svih karakterizacionih tehnika, a ove razlike su bile jošizraženije kod serije sa različitim sadržajem Mg, naročito vrednosti disperznosti Ni0. Primenomrazličitih temperatura redukcije (270 °C, 300 °C, 330 °C, 360 °C i 460 °C) i određivanjem vrednostidisperzije Ni0redukovanih prekursora, utvrđen je optimalni molski odnos nNi:nSiO2. Optimalnatemperatura redukcije ovog prekursora (nNi:nSiO2 = 0,25) određena je na osnovu rezultata katalitičkihtestova parcijalne hidrogenizacije suncokretovog ulja. Na ovoj temperaturi (345 °C) su redukovanisvi prekursori i ispitani su u katalitičkim testovima, nakon čega je određivan sadržaj masnih kiselinaparcijalno hidrogenizovanog suncokretovog ulja gasno-hromatografskom analizom. Utvrđeno je danajveću aktivnost pokazuje katalizator sa molskim odnosom nNi:nSiO2 = 0,25 i nMg:nNi = 0,1. Ovim jepokazano da je moguće sintetisati aktivni nikleni katalizator za hidrogenizaciju suncokretovog uljaupotrebom perlita kao nosača i magnezijuma kao promotora

Opis (srp)

Fizička hemija - Fizička hemija materijala, Kataliza i hemijska kinetika, Fizička hemija ukontroli i zaštiti životne sredine / Physical chemistry - Materials physical chemistry, Catalysis and chemical kinetics, Environmentalphysical chemistry Datum odbrane: 22.06.2022.

Opis (eng)

Within the scope of this doctoral dissertation, the synthesis of a nickel catalyst modifiedwith magnesium on perlite as support for the process of hydrogenation of sunflower oil wasinvestigated. To examine the possible activation of the selected perlite support (PF-295), it wastreated in distilled water at 90 °C, in 10% solution of Na2CO3 at 90 °C and in 9 mol/dm3 HCl withreflux at 100 °C. No significant differences in the morphology, texture or structure of the obtainedmaterials were observed.For precursor synthesis, precipitation-deposition method was used with solid Na2CO3 as aprecipitating agent of nickel (nNi:nSiO2 = 1) and magnesium (nMg:nNi = 0.1) species. Synthesis ofNi2+ precursors on various supports, using Mg as a modifier, no significant differences in thesynthesized precursors were also shown, exept the differences observed in the dispersion values(measured by chemisorption of H2). Minor differences in the activity of afterwards synthesizedcatalysts were observed in catalytic tests of the hydrogenation of sunflower oil.Variation of the values of two synthesis parameters (nNi:nSiO2 and nMg:nNi) yielded a series ofprecursors, later characterized by morphological, textural and structural techniques. For different Nicontents, precursors showed an obvious difference in their characterization, while differences incharacterization, especially in Ni0dispersion, were were more obvious for different Mg contents inprecursors. Measuring the dispersion of Ni0at different temperatures (270 °C, 300 °C, 330 °C, 360°C and 460 °C), the optimal molar ratio of nNi:nSiO2 was obtained. Optimal reduction temperature ofthis precursor (nNi:nSiO2 = 0.25) was established by their catalytic activity in partial hydrogenationof sunflower oil. At this temperature (345 °C), all precursors were reduced and tested in catalytichydrogenation of sunflower oil, after which fatty acid composition was determined by gaschromatography. The catalyst with the molar ratio nNi:nSiO2 = 0.25 and nMg:nNi = 0.1 showed thehighest activity. With this it was shown that it is possible to synthesize an active nickel catalyst forthe hydrogenation of sunflower oil using perlite as support and magnesium as promotor.

Jezik

srpski

Datum

2022

Licenca

Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY-NC-ND 3.0 AT - Creative Commons Autorstvo - Nekomercijalno - Bez prerada 3.0 Austria License.

http://creativecommons.org/licenses/by-nc-nd/3.0/at/legalcode

Predmet

OSNO - Opšta sistematizacija naučnih oblasti, Hemijska termodinamika. Hemijska ravnoteža. Hemijska kinetika

Perlite; Ni catalyst, magnesium, hydrogenation, sunflower oil

OSNO - Opšta sistematizacija naučnih oblasti, Hemijska termodinamika. Hemijska ravnoteža. Hemijska kinetika

Perlit; Ni katalizator, magnezijum, hidrogenizacija, suncokretovo ulje