Naslov (srp)

Površinska modifikacija i karakterizacija legura Ti6Al4V i Nimonik 263 laserskim zračenjem u kontrolisanim atmosferama : doktorska disertacija

Autor

Rajčić, Boris M., 1989-

Doprinosi

Milovanović, Dubravka, 1976-
Cvjetićanin, Nikola, 1959-
Kuzmanović, Miroslav, 1967-
Savović, Jelena
Nedić Vasiljević, Bojana, 1983-

Opis (srp)

Predmet proučavanja ove doktorske disertacije je interakcija laserskog zračenja sa leguromTi6Al4V i superlegurom Nimonik 263. Odabrane legure imaju veliku primenu u savremenimtehnologijama. U doktorskoj disertaciji su ispitivani efekti delovanja impulsnog nano-, piko- ifemtosekundnog laserskog zračenja, kao i uticaj različitih energija impulsa i broja primenjenihimpulsa na osobine površinskih promena ispitivanih legura. Dodatno, ispitivana je i interakcijalaserskog zračenja sa legurama u atmosferama azota i argona i uticaj ovih gasova na modifikaciju ipotencijalnu promenu hemijskog sastava površine legura pre i nakon laserskog ozračivanja, a u ciljupotencijalnog poboljšanja fizičkohemijskih i mehaničkih osobina. Takođe, s obzirom na formiranjeplazme u toku ozračivanja legura laserima, proučavana je i emisija plazme primenom tehnikespektroskopije laserski indukovanog zračenja.Za ispitivane legure, određivane su vrednosti parametara površinske hrapavosti gde jeutvrđeno da se vrednost parametra menja u odnosu na hrapavost nemodifikovanih površina legura, au zavisnosti od primenjene kontrolisane atmosfere. Određivani su i parametri kao što su pragoštećenja legura, zone toplotnog dejstva, brzina ablacije i inkubacioni faktori za različiteeksperimentalne uslove. Dodatnim ispitivanjem formiranih struktura (laserski indukovane periodičnepovršinske strukture) nakon laserskog ozračivanja je pokazano da su one najuniformnije i najvišeizražene prilikom femtosekundnog laserskog ozračivanja.Ispitivanja interakcije legure Ti6Al4V i superlegure Nimonik 263 sa laserskim zračenjem jedovela do boljeg razumevanja procesa koji se dešavaju tokom interakcije kao i do potencijalnemogućnosti poboljšanja određenih karakteristika ovih legura pod odgovarajućim eksperimentalnimuslovima.

Opis (srp)

Fizička hemija - Fizička hemija – materijali, fizička hemija - spektrohemija / Physical chemistry - Physical chemistry – material science; Physical chemistry – spectrochemistry Datum odbrane: 30.06.2022.

Opis (eng)

The subject of research of this doctoral dissertation is the interaction of laser irradiation withthe alloy Ti6Al4V and superalloy Nimonic 263. The selected alloys have great utilization in moderntechnologies. This dissertation examines the effects of pulsed nano-, pico-, and femtosecond laserirradiation, as well as impact of different pulse number and energies on the properties of surfacechanges of the tested alloys. Additionally, the interaction of laser irradiation with alloys in nitrogenand argon atmospheres, and the impact of these gases on modification and potential change in thechemical composition of the surface of alloys before and after laser irradiation was investigated, inorder to potentially improve physicochemical and mechanical features. Also, given the formation ofplasma during the laser irradiation of alloys, plasma emission was also studied using laser-inducedbreakdown spectroscopy technique. The values of surface roughness parameters, for the alloys tested, were determined and foundout that this value changes in relation to the roughness of the alloy’s unmodified surfaces, dependingon the controlled atmosphere applied. Parameters such as the threshold fluence, heat affected zoneand the incubation factor have been also determined for different experimental conditions. Additionalexamination of the formed structures (laser induced periodic surface structures) after the laserirradiation showed that these structures were most uniform and pronounced after the femtosecondlaser irradiation. The study of the interaction between alloys and laser irradiation have led to a betterunderstanding of the processes that occur during the interaction as well as the potential improvementof certain features of these alloys under given conditions.

Jezik

srpski

Datum

2022

Licenca

Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY-NC-ND 3.0 AT - Creative Commons Autorstvo - Nekomercijalno - Bez prerada 3.0 Austria License.

http://creativecommons.org/licenses/by-nc-nd/3.0/at/legalcode

Predmet

OSNO - Opšta sistematizacija naučnih oblasti, Hemijska termodinamika. Hemijska ravnoteža. Hemijska kinetika

Ti6Al4V, Nimonik 263, TEA CO2 laser, Nd:YAG laser, Ti:Safirni laser, laserski indukovane periodične površinske strukture, modifikacija i karakterizacija površina, kontrolisana atmosfera, spektroskopija laserski indukovane plazme

OSNO - Opšta sistematizacija naučnih oblasti, Hemijska termodinamika. Hemijska ravnoteža. Hemijska kinetika

Ti6Al4V, Nimonic 263, TEA CO2 laser, Nd:YAG laser, Ti:Sapphire laser, laser induced periodic surface structures, surface modification and characterization, controlled atmospheres, laserinduced breakdown spectroscopy