Naslov (srp)

Procesiranje i karakterizacija polimernih nanovlakana sa antimikrobnim efektom za prevenciju infekcija izazvanih kateterizacijom urinarnog trakta : doktorska disertacija

Autor

Radisavljević, Anđela N., 1985-

Doprinosi

Uskoković, Petar, 1965-
Radojević, Vesna, 1961-
Rajilić-Stojanović, Mirjana, 1978-
Stajić-Trošić, Jasna, 1967-
Stojanović, Dušica B., 1964-

Opis (srp)

U ovoj doktorskoj disertaciji razvijeni su polimerni materijali, nosači biološki aktivnihsupstanci namenjeni za oblaganje urinarnih katetera. Poli(ε-kaprolakton) (PCL) nanovlakna saantibiotikom cefazolinom su procesirana pomoću tri metode elektropredenja. Dobijeninanovlakanasti matovi su otpuštali lek različitom dinamikom i za 30 dana oslobođeno je ~68 %,~43 % i ~5 % iz nanovlaknastih matova dobijenih elektropredenjem iz rastvora, koaksijalnim iemulzionim elektropredenjem, redom. Nanovlakna sa cefazolinom su pokazala antibakterijskodejstvo prema S. aureus i E. coli. Razvijeni su i PCL nanovlaknasti matovi korišćenjem metodeelektropredenja iz rastvora sa četiri koncentracije ekstrakta hajdučke trave. Korišćenjem statističkiplaniranog eksperimenta optimizovani su uslovi sušenja raspršivanjem za dobijanje suvog ekstraktapodesnog za inkorporaciju u polimerni materijal. Sušenje je izvedeno na temperaturi od 130 °C, pribrzini protoka tečnog ekstrakta od 7,5 ml/min sa 1,2 % sadržaja suve materije. Do 98 %inkorporiranih polifenola hajdučke trave oslobođeno je iz PCL nanovlakana tokom pet dana.Nanovlaknasti matovi su pokazali antioksidativnu i antibakterijsku aktivnost prema S. aureus.Dodatak ekstrakta hajdučke trave poboljšao je mehanička svojstva PCL nanovlaknastih matova,evidentno kroz povećanje Jungovog modula elastičnosti (do 5,7 puta), zatezne čvrstoće (do 5,5 puta)i prekidne deformacije (do 1,45 puta).Silikonski i gumeni kateteri obloženi PCL nanovlaknastim matovima sa cefazolinom iliekstraktom hajdučke trave uz adheziv n-butil-2-cijanoakrilat pokazali su dobru mehaničku stabilnosti antibakterijsku aktivnost. U disertaciju su razvijeni materijali pogodni za dobijenje obloženihkatetera koji mogu da spreče razvoj bakterija i infekcije urinarnog trakta.

Opis (srp)

Tehnološko inženjerstvo - Inženjerstvo materijala / Technological Engineering= Material Engineering Datum odbrane: 29.09.2022.

Opis (eng)

Polymeric materials, carriers of biologically active substances, intended for the production ofurinary catheter coatings were developed in this doctoral thesis. Poly(ε-caprolactone) (PCL)nanofibers with antibiotic cefazolin were produced by using three electrospinning methods. Theobtained nanofiber mats showed different dynamics of drug release. After a period of 30 days ~68%,~43% and ~5% of the drug was released from the nanofiber mats obtained by blend electrospinning,co-axial and emulsion electrospinning, respectively. PCL nanofibers with cefazolin suppressed thegrowth of S. aureus and E. coli. Moreover, PCL nanofiber mats containing four differentconcentrations of yarrow extract were processed by using blend electrospinning. Spray dryingparameters for obtaining dry yarrow extract, which is suitable for incorporation in a polymericmaterial, were optimized in a statistically planned experiment. The drying was performed at 130 °C,with a liquid extract (1.2 % of dry matter content) flow rate of 7.5 ml/min. Up to 98 % of the totalpolyphenols were released from the electrospun PCL nanofibers after a period of five days. Nanofibermats showed antioxidant and antibacterial activity against S. aureus. The addition of yarrow extractimproved mechanical properties of PCL nanofibers, evident by an increase in Young’s modulus ofelasticity (up to 5.7 fold), the tensile strength (up to 5.5 fold), and the strain at break (up to 1.45 fold).Silicone and rubber catheters were coated wtih PCL nanofiber mats with cefazolin or yarrowby using adhesive n-butyl-2-cyanoacrylate. The coated catheters showed good mechanical stabilityand antibacterial activity. The materials are suitable for production of coated catheters that couldprevent urinary tract infections.

Jezik

srpski

Datum

2022

Licenca

Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY-NC-ND 3.0 AT - Creative Commons Autorstvo - Nekomercijalno - Bez prerada 3.0 Austria License.

http://creativecommons.org/licenses/by-nc-nd/3.0/at/legalcode

Predmet

OSNO - Opšta sistematizacija naučnih oblasti, Tehnologija

OSNO - Opšta sistematizacija naučnih oblasti, Ispitivanje materijala. Inženjerstvo materijala

poli(ε-kaprolakton); elektropredenje; cefazolin, hajdučka trava; polifenoli; oslobađanje leka; kinetika oslobađanja leka; antibakterijska aktivnost; antioksidativna aktivnost; mehanička svojstva

OSNO - Opšta sistematizacija naučnih oblasti, Tehnologija

OSNO - Opšta sistematizacija naučnih oblasti, Ispitivanje materijala. Inženjerstvo materijala

poly(ε-caprolactone); electrospinning; cefazolin; yarrow; polyphenols; drug release; drug release kinetics; antibacterial activity; antioxidant activity; mechanical properties