Fatigue crack growth in T welded joint of aluminium alloy : doctoral dissertation
Kraedegh, Abubakr M. Abdulgadr.
Sedmak, Aleksandar, 1955-
Radaković, Zoran, 1961-
Grbović, Aleksandar, 1970-
Veg, Emil.
Burzić, Zijah.
U ovom radu su prikazani inicijacija i rast prsline u T spoju ploče od aluminijumske legure AA2024 –T351, zavarenom mešanjem trenjem (Friction Stir Welding - FSW), primenom mehanike loma. Svi analizirani modeli su napravljeni od legure 2024-A351. Osobine materijala i dimenzije u oblasti FSW spoja su usvojene na osnovu dostupnih eksperimenata...
In this present work, application of fracture mechanics is used to present a fatigue crack initiation and growth of friction stir welded (FSW) T joint plate made of aluminum alloy AA2024 –T351. All analyzed models are made from aluminum alloy 2024-T351.The properties of materials in the areas of joints and geometry measures of FSW joint are adopted from available experiments...
Mechanical engineering-Structure integrity Datum odbrane: 29.03.2018.
engleski
2017
Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY 2.0 AT - Creative Commons Autorstvo 2.0 Austria License.
http://creativecommons.org/licenses/by/2.0/at/legalcode
OSNO - Opšta sistematizacija naučnih oblasti, Termička obrada
OSNO - Opšta sistematizacija naučnih oblasti, Ispitivanje materijala. Inženjerstvo materijala
zamorni rast prsline, proširena metoda konačnih elemenata (PMKE), žilavostloma, zavarivanje mešanjem trenjem (FSW), softver, zavarena konstrukcija, LEML – linearnoelastičnamehanika loma, K – faktor intenziteta napona
OSNO - Opšta sistematizacija naučnih oblasti, Termička obrada
OSNO - Opšta sistematizacija naučnih oblasti, Ispitivanje materijala. Inženjerstvo materijala
fatigue crack growth, extended Finite Element Method (XFEM), fracture toughness, Friction Stir Welding (FSW), software, welded construction,LEFM - linear-elastic fracture mechanics, stress intensity factor- K