Naslov (srp)

Modifikacija strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja : doktorska disertacija

Autor

Milićević, Bojana R.

Doprinosi

Stojković Simatović, Ivana
Dramićanin, Miroslav
Šljukić-Paunković, Biljana
Đorđević, Vesna
Minić-Popović, Dragica

Opis (srp)

U ovoj doktorskoj disertaciji prikazana je temeljna studija modifikovanja strukturnih, morfoloških i optičkih svojstava anatas TiO2 nanočestica dopiranjem trovalentnim jonima retkih zemalja: prazeodijuma, neodijuma, samarijuma, europijuma, disprozijuma, terbijuma, holmijuma, erbijuma i tulijuma, pri koncentraciji od 1 at.%. Pomenuti materijali sintetisani su sol-gel tehnikom i žareni na temperaturi od 420 ºC. Strukturna svojstva nedopiranog anatas TiO2 kao i TiO2 dopiranоg jonima retkih zemalja ispitivana su rendgenskom difrakcionom analizom. Utvrđeno je da se sol-gel sintezom dobijaju čiste anatasne kristalne strukture sa veličinom kristalita od svega nekoliko nanometara. Uticaj jona retkih zemalja u anatasnoj kristalnoj strukturi titan-dioksida ogleda se u značajnom porastu specifične površine čestica. Takođe, sintetisani su nanoprahovi TiO2 koloidnom tehnikom u cilju korelisanja različitih metoda sinteza sa strukturnim, morfološkim i optičkim svojstvima...

Opis (srp)

Fizička hemija - Fizička hemija materijala / Physical chemistry - Physical chemistry of materials Datum odbrane: 02.10.2017.

Opis (eng)

The primary aim of this thesis is to explain the modification of structure, morphology and optical properties of anatase TiO2 nanoparticles doped with trivalent rare-earth ions: praseodymium, neodymium, samarium, europium, terbium, dysprosium, holmium, erbium, and thulium, with the concentration of 1 at.%. These materials were synthesized by the sol-gel technique and further annealed at 420 °C. Structural properties of anatase TiO2 and TiO2 doped with trivalent rare-earth ions are studied by X-ray diffraction analysis. It was confirmed that pure anatase TiO2 with the crystallite size of only a few nanometers was obtained by sol-gel synthesis. The incorporation of rare earth ions in the anatase TiO2 is reflected in the significant increase of the specific surface area of TiO2 nanopowders doped with rare-earth ions in comparison with undoped TiO2. Also, the TiO2 nanopowders were synthesized by a colloid technique to correlate the different methods of synthesis with structural, morphological and optical properties...

Jezik

srpski

Datum

2017

Licenca

Ovo delo je licencirano pod uslovima licence
Creative Commons CC BY-NC-ND 2.0 AT - Creative Commons Autorstvo - Nekomercijalno - Bez prerada 2.0 Austria License.

http://creativecommons.org/licenses/by-nc-nd/2.0/at/legalcode

Predmet

OSNO - Opšta sistematizacija naučnih oblasti, Nanostrukture. Nanotehnologija

Titan(IV)-oxide, rare-earth ions, luminescent nanomaterials, lithium co-doping, photocatalytic nanomaterials

OSNO - Opšta sistematizacija naučnih oblasti, Nanostrukture. Nanotehnologija

titan(IV)-oksid, joni retkih zemalja, luminescentni materijali, Li+-kodopiranje, fotokatalitički materijali